新能源硅钢电工钢 B35AV1900

电工钢硅钢片5 剪切适应性钢带应便于进行剪切或冲压 ,以保证在任何位置将钢带剪切成通常的形状。7 技术要求7.1 磁性能在 6.3 条件下提供的产品的磁性能应符合表 3 和表 4 的规定。时效后的磁性能要求，由供需双方在订货时协商，并在合同中注明。表 3 普通型 A、江西宜春本地应力退火型 AR、江西宜春本地型 AH 产品磁性能和技术特性类型 牌号公称厚度mm 比总损耗名义值P1.5/50 W/kg 比总损耗P1.5/50 W/kg小磁极化强度J5000a T比总损耗各向异性T1.5/50b ％小叠装系数小弯曲次数约定密度kg/dm3普通型B35A2000.352.00 2.00 1.62 ±170.952 7.60B35A210 2.10 2.10 1.62 ±17 2 7.60B35A230 2.30 2.28 1.64 ±17 2 7.60B35A250 2.50 2.45 1.64 ±17 2 7.60B35A270 2.70 2.65 1.64 ±17 2 7.65B35A300 3.00 2.90 1.64 ±17 3 7.65B35A360 3.60 3.20 1.65 ±17 3 7.65B35A440 4.40 3.40 1.67 ±17 3 7.70B50A2300.502.30 2.30 1.64 ±170.972 7.60B50A250 2.50 2.48 1.64 ±17 2 7.60B50A270 2.70 2.65 1.64 ±17 2 7.60B50A290 2.90 2.85 1.64 ±17 2 7.60B50A310 3.10 3.00 1.65 ±14 3 7.65B50A350 3.50 3.20 1.65 ±12 5 7.65B50A400 4.00 3.30 1.66 ±12 5 7.70B50A470 4.70 4.20 1.67 ±10 10 7.70B50A600 6.00 4.70 1.68 ±10 10 7.75B50A700 7.00 5.50 1.71 ±10 10 7.80B50A800 8.00 5.80 1.71 ±10 10 7.80B50A1000 10.00 6.00 1.74 ±8 10 7.85B50A1300 13.00 7.00 1.74 ±8 10 7.85B65A3100.653.10 3.05 1.64 ±150.972 7.60B65A350 3.50 3.45 1.65 ±14 2 7.60B65A400 4.00 3.95 1.66 ±14 2 7.65B65A470 4.70 4.60 1.67 ±12 5 7.65B65A530 5.30 5.20 1.68 ±12 10 7.70B65A600 6.00 5.90 1.68 ±10 10 7.75B65A700 7.00 6.90 1.69 ±10 10 7.75B65A800 8.00 7.90 1.71 ±10 10 7.80B65A1000 10.00 9.90 1.71 ±10 10 7.80B65A1300 13.00 12.90 1.72 ±8 10 7.

电工钢硅钢片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example:

电工钢硅钢片：取向电工钢产品表面涂层种类及特征绝缘涂层种类 代号 特征无机涂层 S涂层为磷酸盐和二氧化硅为主的无机成分混合物。该涂层具有较高的耐热性，在干的氮气或者干的氮氢混合保护气氛中可以承受 850℃应力退火。对绝缘油、江西宜春同城清漆、江西宜春同城机械油、江西宜春同城制冷气体等有高耐腐性。无 Cr 环保涂层 H 涂层成分中不含 Cr 元素无涂层 — 表面没有玻璃膜底层和绝缘涂层，适用于直接轧制晶粒取向电工钢极薄带。6 一般要求6.1 生产工艺产品的生产工艺和化学成分由制造方决定。